Characterization of Lamina and Interlaminar Damage in Graphite/Epoxy Composites by the Deply Technique /
A unique technique is described for separating a cured graphite/epoxy composite into its individual laminae while maintaining the integrity of each lamina. The use of this technique provides information heretofore unavailable for fracture and failure analysis. Examples of damage characterization usi...
Main Author: | Freeman, SM (Author) |
---|---|
Corporate Authors: | Composite Materials: Testing and Design (6th Conference) Phoenix, Arizona), ASTM International, American Society for Testing and Materials |
Format: | Conference Proceeding Book |
Language: | English |
Published: |
West Conshohocken, Pa. :
ASTM International,
1982
|
Subjects: |
Similar Items
-
Determination of Crack Propagation Directions in Graphite/Epoxy Structures /
by: Grove, RA, et al.
Published: (1987) -
Mode II interlaminar fracture toughness and fatigue characterization of a graphite epoxy composite material /
by: O'Brien, T. Kevin, et al.
Published: (2010) -
Interlaminar Fracture Toughness and Real-Time Fracture Mechanism of Some Toughened Graphite/Epoxy Composites /
by: Bradley, WL, et al.
Published: (1987) -
Correlations Between Micromechanical Failure Processes and the Delamination Toughness of Graphite/Epoxy Systems /
by: Hibbs, MF, et al.
Published: (1987) -
Comparisons of Various Configurations of the Edge Delamination Test for Interlaminar Fracture Toughness /
by: Johnston, NJ, et al.
Published: (1987)